Marine cable

Wires & Cables www.siechem.com Property General PVC 70°C FRLS PVC 70°C HFFR 90°C XLPE (Chemical Curing) 90°C Specially Formulated EBXL - ZHLS + FR 0 (XLPO) 120 C For Marine Cables Heat ageing at 80°C for 7 days 80°C for 7 days 80°C for 7 days 135°C for 7 days 158°C for 7 days 158°C for 7 days Variation in Tensile strength & elongation at break after ageing. ±20% ±20% ±20% ±25% ±15% ±15% Hot deformation Max 50% 50% 50% 50% <25% <25% Heat shock test Result At 150°C for 1 hr shall not crack at 200°C for 1 hr insulation cracks At 150°C for 1 hr shall not crack at 200°C for 1 hr insulation cracks At 150°C for 1 hr shall not crack at 200°C for 1 hr insulation cracks At 150°C for 1 hr shall not crack at 200°C for 1 hr insulation cracks At 240°C for 3 hrs shall not crack At 240°C for 3 hrs shall not crack Shrinkage Max. 4% 4% 4% 4% 2% 0.50% Operating temp. 70°C 70°C -40°C to 90°C -45°C to 120°C & 150°C Short circuit temp. 160°C 160°C 280°C & 300°C 280°C & 300° Soldering iron resistance Insulation melts and emmits smoke Insulation melts and emmits smoke Insulation melts Melts Reasonably Resistant Resistant 90°C -15°C to 120°C 250°C 160°C Thermal properties of EBXL 120°C cables are superior and conventional PVC, FRLS, HFFR & XLPE-90°C stand no comparison. THERMAL PROPERTIES FIRE PROPERTIES Smoke density max. > 80 % 60% 20% NA <10% <10% Toxicity Index High High <5 >10 <4 <4 Acid gas Emmission Max. >25% 20% Nil NA Nil Nil Flammability Melt and Drip Melt and drip Melt and drip Melt and Drip Do not melt or drip Do not melt or drip Flame propagation High High Moderate High Fire properties of EBXL XLPO cables stands tall compared with the PVC, FRLS, HFFR & XLPE cables. Very low High From the above comparison it is evident that in every respect Electron Beam Cured Zero Halogen Polyolefin Cables shows better performance compared to PVC based cables. EBXL - XLPE 120°C Hence it is proposed to go in for new generation high technology, indigenously manufactured EBXL wires and cables. The details given above are for guidance only and actual results may vary marginally from different sources. 223